Acrylic film and laminates comprising the same

ABSTRACT

To provide an acrylic film, composed of a resin composition (C) that includes an acrylic graft copolymer (A) containing an acrylic ester rubber-like polymer and a methacrylic polymer (B) containing 80% by weight or more of methyl methacrylate, wherein (1) the content of the acrylic ester rubber-like polymer in the resin composition (C) is 5% by weight or more and 30% by weight or less, (2) the average particle size of the acrylic ester rubber-like polymer is 500 to 2000 Å, (3) the relationship between the average particle size d (Å) of the acrylic ester rubber-like polymer and the amount w (% by weight) of crosslinking agent used in the acrylic ester rubber-like polymer satisfies the following equation: 0.002d≦w≦0.005d, (4) the graft ratio of the acrylic graft copolymer (A) is 30% or more and 200% or less, and (5) the reduced viscosity of methyl ethyl ketone soluble matter in the resin composition (C) is 0.2 to 0.8 dl/g.

This application is a national phase patent application of PCT/JP2002/013279 filed on Dec. 19, 2002, claiming priorities of Japanese patent application No. 2002-300664 filed on Oct. 15, 2002 and Japanese patent application No. 2002-300665 filed Oct. 15, 2002.

TECHNICAL FIELD

The present invention relates to a special acrylic film and an acrylic film laminate, in particular to an acrylic film laminate produced by injection molding.

BACKGROUND ART

Methods for decoration of the surface of plastic or metal parts include, for example, a direct printing process and a decalcomania process. However, the direct printing process has a problem of being unsuitable for molded products having a complex shape, whereas the decalcomania process has a problem of being costly. In the meantime, there are methods for decoration of the surface of plastic or metal products at low costs: for example, a film insert molding process in which a base resin is injection molded while a film of acrylic resin etc. having been shaped by vacuum forming in advance is inserted into a cavity of an injection molding die; and a film in-mold molding process in which a base resin is injection molded while a film having not been shaped is inserted into a cavity of an injection molding die. And there have been proposed various methods for producing acrylic films suitable for this application. For example, there are known a method in which the reduced viscosity of plastic polymer, the particle size of rubber-containing polymer, the rubber content etc. are specified (Japanese Patent Laid-Open No. 8-323934) and a method in which the reduced viscosity of acrylic polymer and the content of multi-layer structure acrylic polymer are specified (Japanese Patent Laid-Open Nos. 10-279766 and 10-306192). The films produced by these methods are known to excel in surface hardness, transparency and moldability. However, these patent specifications do not describe the problem of stress-whitening occurring in the films or cracks occurring at the time of film cutting.

For the problem of stress-whitening occurring in films, Japanese Patent Laid-Open No. 2002-80678 states that the problem can be solved by specifying the particle size of rubber-like polymer used to be less than 2000 Å. In this document, vacuum forming is performed at pre-heating temperatures as relatively high as 125 to 145° C.; however, some of the films described in the document undergoes stress-whitening at pre-heating temperature of 125° C. or 130° C. Stress-whitening is more likely to occur at lower heating temperatures, and even by the method described in this document, a film is hard to form by vacuum forming at temperatures lower than the above described temperatures. This document does not mention at all the problem of cracks occurring in a film when cutting the molding flash at the end portion of the film at finishing step. Specifically, in any one of these films, when laminating the film on a molded product of a complex shape at low temperatures, stress is concentrated in the corner of the film, and the film is likely to undergo whitening, resulting in significant deterioration of its value as a product. These films also have a problem of cracks caused when cutting at a finishing step the molding flash at the end portion of the film laminates obtained by a film insert molding process or film in-mold molding process.

Under these circumstances, the present inventors directed tremendous research efforts toward the development of a film in which stress-whitening hardly occur even by molding at low temperatures and cracks hardly occur at the time of cutting of the film. And they have found that a film, composed of a resin composition that includes a multi-layer structure acrylic polymer using a special acrylic ester rubber-like polymer and a methacrylic polymer, undergoes less stress-whitening even by molding at low temperatures and has high surface hardness, excellent transparency, also excellent transparency even after heating and excellent weatherability, and its elongation at the time of tensile breakage is high and its moldability, surface properties and processability (cracks are less likely to occur at the time of film cutting) are all excellent.

DISCLOSURE OF THE INVENTION

The present invention relates to an acrylic film composed of a resin composition (C) that includes an acrylic graft copolymer (A) containing an acrylic ester rubber-like polymer and a methacrylic polymer (B) containing 80% by weight or more of methyl methacrylate, wherein

-   (1) the content of the acrylic ester rubber-like polymer in the     resin composition (C) is 5% by weight or more and 30% by weight or     less, -   (2) the average particle size of the acrylic ester rubber-like     polymer is 500 to 2000 Å, -   (3) the relationship between the average particle size d (Å) of the     acrylic ester rubber-like polymer and the amount w (% by weight) of     a crosslinking agent used in the acrylic ester rubber-like polymer     satisfies the following equation:     0.002d≦w≦0.005d, -   (4) the graft ratio of the acrylic graft copolymer (A) is 30% or     more and 200% or less, and -   (5) the reduced viscosity of methyl ethyl ketone soluble matter in     the resin composition (C) is 0.2 to 0.8 dl/g.

Preferably, the relationship between the average particle size d (Å) of the acrylic ester rubber-like polymer and the amount w (% by weight) of the crosslinking agent used in the acrylic ester rubber-like polymer satisfies the following equation: 0.0025d≦w≦0.005d.

More preferably, the content of the acrylic ester rubber-like polymer in the resin composition (C) is 15% by weight or more and 30% by weight or less.

Furthermore preferably, the content of the acrylic ester rubber-like polymer in the resin composition (C) is more than 20% by weight and 30% by weight or less.

Preferably, the acrylic graft copolymer (A) is prepared by: graft polymerizing a monomer mixture containing 86% by weight or more of a methacrylic ester onto the acrylic ester rubber-like polymer in a first step; and graft polymerizing a monomer mixture containing 85% by weight or less of a methacrylic ester onto the resultant graft polymer in a second step.

The present invention also relates to a laminate of the above acrylic film.

Preferably, the above laminate is produced by injection molding.

BEST MODE FOR CARRYING OUT THE INVENTION

The resin composition (C) used in the present invention includes an acrylic graft copolymer (A) containing an acrylic ester rubber-like polymer and a methacrylic polymer (B) containing 80% by weight or more of methyl methacrylate. The resin composition (C) can be obtained by first polymerizing the acrylic graft copolymer (A) and the methacrylic polymer (B), separately, and then mixing the copolymer and the polymer. The preparation of these copolymer and polymer can be carried out in the same reactor in such a manner as to first prepare the acrylic graft copolymer (A) and subsequently prepare the methacrylic polymer (B). The copolymer (A) and the polymer (B) can be mixed in the form of latex, powder, beads or pellets.

The acrylic graft copolymer (A) used in the present invention is obtained by polymerizing a monomer mixture containing a methacrylic ester as a chief ingredient in the presence of an acrylic ester rubber-like polymer (a cross linked rubber-like polymer containing acrylic ester as a chief ingredient).

The acrylic graft copolymer (A) used in the present invention can also be obtained by graft polymerizing a monomer mixture containing 86% by weight or more of a methacrylic ester in a first step and then graft polymerizing a monomer mixture containing 85% or less of a methacrylic ester in a second step, in the presence of an acrylic ester rubber-like polymer.

The acrylic ester rubber-like polymer in the acrylic graft copolymer is prepared by polymerizing a monomer mixture including: 60 to 99% by weight of an acrylic ester; 0 to 30% by weight of another copolymerizable vinyl monomer and a specific amount of a copolymerizable crosslinking agent. This preparation may be carried out by mixing all the monomers or carried out in two or more steps while varying the monomer composition.

As the acrylic ester used, those having 1 to 12 carbon atoms in the alkyl group are preferable from the viewpoint of polymerizability and cost. Concrete examples of such acrylic esters include: methyl acrylate, ethyl acrylate, propyl acrylate, butyl acrylate, 2-ethylhexyl acrylate and n-octyl acrylate. These monomers may be used alone or in combination.

The content of the acrylic ester in the acrylic ester rubber-like polymer is preferably 60 to 99% by weight, more preferably 70 to 99% by weight, much more preferably 80 to 99% by weight and most preferably 85 to 99% by weight. If the content is less than 60% by weight, the impact resistance tends to deteriorate, the elongation at the time of tensile breakage also tends to be lowered, and cracks tend to occur at the time of film cutting, whereas if the content is more than 99% by weight, the pencil hardness and transparency of the resultant film tend to be lowered.

As the other copolymerizable vinyl monomer, methacrylic esters are particularly preferable from the viewpoint of weathering resistance and transparency. Concrete examples of methacrylic esters include methyl methacrylate, ethyl methacrylate, propyl methacrylate and butyl methacrylate. Aromatic vinyls (e.g. styrene, methylstyrene, etc.) and vinyl cyanideds (e.g. acrylonitrile, methacrylonitrile, etc.) are also preferable. These monomers may be used alone or in combination.

The content of the other copolymerizable vinyl monomer in the acrylic ester rubber-like polymer is preferably 0 to 30% by weight and more preferably 0 to 15% by weight. If the content is more than 30% by weight, the moldability, processability, transparency and surface properties of the film tend to deteriorate.

As the copolymerizable crosslinking agent, conventional one maybe used. Concrete examples of such crosslinking agents include allyl methacrylate, allyl acrylate, triallyl cyanurate, triallyl isocyanurate, diallyl phthalate, diallyl malate, divinyl adipate, divinyl benzene, ethylene glycol dimethacrylate, diethylene glycol methacrylate, triethylene glycol dimethacrylate, trimethylolpropane trimethacrylate, tetramethylolmethane tetramethacrylate, dipropylene glycol dimethacrylate and the acrylates thereof. These crosslinking agents may be used alone or in combination.

The content of the copolymerizable crosslinking agent in the acrylic ester rubber-like polymer largely affects the average particle size of the acrylic ester rubber-like polymer and the stress-whitening, elongation at the time of tensile breakage and transparency of the film. Accordingly, it is important that the average particle size d (Å) of the acrylic ester rubber-like polymer and the content of the crosslinking agent w (% by weight) satisfy the following equation: 0.002d≦w≦0.005d.

The minimum of the average particle size of the acrylic ester rubber-like polymer is preferably 500 Å and more preferably 600 Å. The maximum of the same is 2000 Å, preferably 1800 Å, more preferably 1600 Å, much more preferably 1500 Å, and further more preferably 1200 Å. If the average particle size is less than 500 Å, the impact resistance and elongation at the time of tensile breakage of the film tend to deteriorate and cracks tend to occur at the time of film cutting, whereas if the average particle size is more than 2000 Å, stress-whitening tends to occur in the resultant film, the transparency of the film tend to be lowered, and the transparency of the film after vacuum forming also tends to be lowered.

The content of the crosslinking agent is preferably in the range shown by the above equation, more preferably 0. 0025d≦w≦0.005 d and much more preferably 0.0025d≦w≦0.0045d. If the relationship between the content w of the crosslinking agent and the average particle size d of the acrylic ester rubber-like polymer is in the range of 0. 002d>w or w>0.005d, stress-whitening tends to occur, the impact resistance and transparency of the film tend to deteriorate, the elongation at the time of tensile breakage tends to be lowered, cracks tend to occur at the time of film cutting, and the processability of the film tends to deteriorate.

The acrylic graft copolymer (A) used in the present invention is obtained by polymerizing a monomer mixture containing a methacrylic ester as a chief ingredient in the presence of the above described rubber-like polymer. Preferably, the acrylic graft copolymer (A) is obtained by polymerizing 95 to 25 parts by weight of a monomer mixture containing a methacrylic ester as a chief ingredient in the presence of 5 to 75 parts by weight of an acrylic ester rubber-like polymer in one or more steps. The content of the methacrylic ester in the graft copolymer composition (monomer mixture) is preferably 50% by weight or more and more preferably 60% by weight or more. If the content is less than 50% by weight, the hardness and stiffness of the resultant film tend to deteriorate.

The monomers used in the graft copolymerization include methacrylic esters and acrylic esters. And concrete examples of such monomers include those used in the above described acrylic ester rubber-like polymer. These monomers may be used alone or in combination.

When intending to obtain the acrylic graft copolymer (A) is to be obtained by graft polymerization in two steps, the monomer mixture containing 86% by weight or more of a methacrylic ester is graft polymerized in the presence of the above described acrylic ester rubber-like polymer in the first step and the monomer mixture containing 85% by weight or less of a methacrylic ester is graft polymerized in the second step.

The content of the methacrylic ester in the monomer mixture graft polymerized in the first step is preferably 86% by weight or more, more preferably 88% by weight or more and most preferably 90% by weight or more. The content of the methacrylic ester in the monomer mixture graft polymerized in the second step is preferably 85% by weight or less, more preferably 83% by weight or less and most preferably 80% by weight or less. If the content of the methacrylic ester in the monomer mixture graft polymerized in the first step is less than 86% by weight and that of the methacrylic ester in the monomer mixture graft polymerized in the second step is more than 85% by weight, stress-whitening is more likely to occur, and therefore the contents in such ranges are not preferable.

Preferably, the acrylic graft copolymer (A) is obtained by polymerizing 95 to 25 parts by weight of the monomer mixture containing a methacrylic ester as a chief ingredient in the presence of 5 to 75 parts by weight of the acrylic ester rubber-like polymer in two or more steps. The content of the monomer mixture polymerized in the presence of 5 to 75 parts by weight of the acrylic ester rubber-like polymer is preferably 90 to 5 parts by weight in each of the first and second steps and more preferably 85 to 10 parts by weight in each of the first and second steps. If the amount is outside the above range, the transparency, pencil hardness, moldability and processability of the film tend to deteriorate. The content of a methacrylic ester in the graft copolymer composition (monomer mixture) is preferably 50% by weight or more and more preferably 60% by weight or more. If the content is less than 50% by weight, the hardness and stiffness of the resultant film tend to deteriorate.

When polymerizing the monomer mixture containing a methacrylic ester as a chief ingredient onto the acrylic ester rubber-like polymer, some of the monomer mixture does not undergo graft reaction with the acrylic ester rubber-like polymer to produce an un-grafted polymer component. This component constitutes the whole or part of the methacrylic polymer (B). The graft copolymer is not dissolved in methyl ethyl ketone. The lower limit of the graft ratio to the acrylic ester rubber-like polymer is 30%, preferably 50% and more preferably 80%. The upper limit of the graft ratio is 200% and preferably 150%. If the graft ratio is less than 30%, the transparency of the film and the elongation at the time of tensile breakage of the film tend to be lowered and cracks tend to occur at the time of film cutting, whereas if the graft ratio is more than 200%, the melting viscosity at the time of film molding becomes high and the moldability of the film tends to deteriorate.

The methacrylic polymer (B) used in the present invention contains methyl methacrylate as a polymerizable ingredient. The content of methyl methacrylate is 80% by weight or more, preferably 90% by weight or more and more preferably 92% by weight or more. If the content of methyl methacrylate is less than 80%, the hardness and stiffness of the resultant film tends to deteriorate.

The lower limit of the content of the acrylic ester rubber-like polymer in the resin composition (C) used in the present invention is preferably 5% by weight, more preferably 10% by weight, much more preferably 15% by weight and most preferably more than 20% by weight. The upper limit of the content is preferably 30% by weight, more preferably 25% by weight and most preferably 23% by weight. If the content is less than 5% by weight, the elongation at the time of tensile breakage of the film tends to be lowered, cracks are more likely to occur at the time of film cutting and stress-whitening tends to occur in the film, whereas if the content is more than 30% by weight, the hardness and stiffness of the resultant film tend to deteriorate.

The reduced viscosity of the methyl ethyl ketone-soluble matter in the resin composition (C) used in the present invention is preferably 0.2 to 0.8 dl/g and more preferably 0.2 to 0.7 dl/g. If the reduced viscosity is less than 0.2 dl/g, the elongation at the time of tensile breakage of the resultant film is lowered, cracks are likely to occur at the time of film cutting, and the solvent resistance tends to deteriorate, whereas if the reduced viscosity is more than 0.8 dl/g, the moldability of the film tends to deteriorate.

The process for preparing the acrylic graft copolymer (A) and methacrylic polymer (B) used in the present invention is not particularly limited and, for example, emulsion polymerization, suspension polymerization and bulk polymerization are applicable.

In the emulsion polymerization, a conventional polymerization initiator is used. Concrete examples of such initiators include: inorganic peroxides such as potassium persulfate and sodium persulfate; and organic peroxides such as cumene hydroperoxide and benzoyl peroxide. Oil-soluble initiators such as azobisisobutyronitrile can also be used. These initiators may be used alone or in combination.

These initiators maybe used in combination with a reducing agent, such as sodium sulfite, sodium thiosulfate, sodium formaldehyde, sulfoxylate, ascorbic acid or ferrous sulfate, as a conventional redox initiator.

The surfactant used in the emulsion polymerization is not particularly limited, either, and any conventional surfactant for emulsion polymerization can be used. Examples of such surfactants include: anionic surfactants such as sodium alkylsulfate, sodium alkylsulfonate, sodium alkylbenzenesulfonate, dioctyl sodium sulfosuccinate and sodium laurate; and nonionic surfactants such as reaction products of alkyl phenols and ethylene oxide. These surfactants may be used alone or in combination.

The resin composition can be separated and collected from the polymer latex obtained by the above described copolymerization through the steps of conventional solidification and cleaning or through the treatment by spray drying or freeze-drying.

The resin composition (C) obtained in accordance with the present invention is particularly effective as a film and can be satisfactorily processed by conventional melt extrusion techniques such as inflation or T die extrusion, or calendering, or solvent casting technique. The thickness of the film is suitably about 30 to 500 μm and preferably 50 to 300 μm. Films having more excellent surface properties can be obtained, if necessary, by bringing both sides of the film into contact with a roll or a metal belt, particularly a roll or a metal belt heated to temperatures above glass transition temperature at the time of film molding by using the resin composition (C).

To the resin composition (C) of the present invention, additives for coloring, such as inorganic or organic pigments or dyes, or additives for stabilizing the film against heat or light, such as anti-oxidant, heat stabilizer, ultraviolet absorber or ultraviolet stabilizer, may be added. These additives may be used alone or in combination.

The method of producing laminates using the film of the present invention is not limited to any specific one; however, such laminates are preferably produced by a film insert molding process or film in-molding molding process, like those described in Japanese Patent Publication Nos. 63-6339, 4-9647, Japanese Patent Laid-Open Nos. 7-9484, 8-323934 and 10-279766. Specifically, laminates are produced by: first inserting a film having been shaped in advance by vacuum forming etc. or a film having not been shaped into an injection molding die; closing the injection molding die with the film held between the two parts of the die to clamp the film; and injecting base resin into the molding die, so that the film is molten on the surface of the molded part of the base resin and integrated therewith. In the injection molding, the injection molding conditions such as resin temperature and injection pressure are properly set taking the types of the base resin etc. into consideration.

The base resin that constitutes the acrylic laminates obtained in accordance with the present invention is required to be able to melt and adhere to acrylic film. Examples of such base resins include ABS resin, AS resin, styrene resin, polycarbonate resin, vinyl chloride resin, acrylic resin, polyester resin, and resins containing these resins as a chief ingredient.

EXAMPLES

In the following the present invention will be described by examples and comparative examples; however, it should be understood that these examples are not intended to limit the present invention. The terms “parts” and “%” used in examples and comparative examples mean parts by weight and % by weight, respectively. The abbreviations used represent the following substances.

OSA: dioctyl sodium sulfosuccinate

BA: butyl acrylate

MMA: methyl methacrylate

CHP: cumene hydroperoxide

tDM: tert-dodecyl mercaptan

EA: ethyl acrylate

AMA: allyl methacrylate

The characteristics were obtained and the evaluation was made by the following methods under the following conditions. (Average particle size of acrylic ester rubber-like polymer)

A film was subjected to ruthenium staining and observed with a transmission electron microscope. The particle size was measured for 500 particles and the average value of the measurements was obtained (unit: Å).

(Graft Ratio G)

The powder prepared in reference examples was dissolved in methyl ethyl ketone and the insoluble matter was separated from the soluble matter. The insoluble matter was taken as graft polymer and the graft ratio was obtained by the following equation (unit: %):

G=(weight of insoluble matter−weight of rubber-like polymer)/weight of rubber-like polymer×100.

(Reduced Viscosity)

The powder prepared in reference examples was dissolved in methyl ethyl ketone and the insoluble matter was separated from the soluble matter. The soluble matter was dissolved in N,N-dimethyl formamide so that the content of the soluble matter was 0.3% by weight. The viscosity at 30° C. was measured using an Ubbelohde tube (unit: dl/g).

(Tensile Strength, Elongation at the Time of Tensile Breakage)

Film was cut out in JIS dumbbell shape, and the tensile strength and elongation at the time of tensile breakage of the dumbbell specimen were measured with Autograph (Shimadzu) at 23° C. at a tensile speed of 50 mm/min (unit: tensile strength MPa, elongation at the time of tensile breakage %).

(Stress-Whitening)

An operation was performed once at 23° C. in which film (100 μm thick, cut to 210 mm×290 mm) was folded in two and held down firmly with fingers to give it a fold. Then the whitening occurring on the film was observed and evaluated based on the following criteria.

-   ◯: No whitening is observed on the fold. -   Δ: Opaque white (slight whitening) is observed on part of the fold. -   ×: Whitening is significant.     (Transparency)

The haze of film was measured in accordance with JIS K 6714 (unit: %).

(Transparency After Heating)

The haze of film was measured in accordance with JIS K 6714 after heating the film at 160° C. for 1 minute, and the difference in haze before and after heating was evaluated based on the following criteria.

-   ◯: The difference in haze before and after heating is less than 0.5. -   Δ: The difference in haze before and after heating is 0.5 or more     and less than 1.0. -   ×: The difference in haze before and after heating is 1.0 or more.     (Pencil Hardness)

The pencil hardness of film was measured in accordance with JIS K 5400.

(Moldability of Film)

Film molding was performed continuously for 3 hours under the same conditions as those of examples 1 to 17 and comparative examples 1 to 7 and the state of molding was observed (the center portion of film was cut off every 15 minutes to measure the thickness of the film). The moldability was evaluated based on the following criteria.

-   ◯: The thickness of film is uniform (100±5 μm) and film can be     molded without causing film breakage. -   Δ: The thickness of film is almost uniform (100±10 μm) and film can     be molded without causing film breakage. -   ×: The thickness of film is not uniform and film breaks.     (Surface Properties of Film)

The surface of a film 1 m×1 m in size (100 μm thick) was observed and the surface properties were judged by the standards for fish eye, die line and carbonized resin which were used as a base for acceptance of the film.

The standard for fish eye used as a base for acceptance of film is that the number of fish eyes observed is 1000 or less and the term “significant” means that the number of fish eyes observed is 10,000 or more.

The standard for die line used as a base for acceptance of film is that the number of die lines less than 10 cm long is 5 or less and the term “significant” means that die line 1 m or more long is observed.

The standard for carbonized resin used as a base for acceptance of film is that the film is not discolored or the number of carbonized resin observed is 5 or less and the term “significant” means that carbonized resin is obvious and the number of carbonized resin is 50 or more.

-   ◯: The surface of film satisfies the standards for all of the above     3 items. -   Δ: The surface of film does not satisfy the standard for only one     item, but the evaluation for the rejected item is not “significant”. -   ×: The surface of film does not satisfy the standards for two or     more of the above 3 items, or it is evaluated as “significant” for     any one of the above 3 items.     (Processability of Film)

Film (100 μm thick) was placed on a flat stand and cut to 20 cm in various directions with a cutter knife (with an edge 0.38 mm thick) using force sufficient to cut the film and the processability of the film was evaluated based on the following criteria.

-   ◯: No crack was observed. -   Δ: Cracks were observed (less than 5 cracks which were 5 mm or less     long). -   ×: Cracks were significantly observed (5 or more cracks which were 5     mm or less long, or at least one crack 5 mm or more long was     observed).

Reference Examples 1 to 18

The following substances were fed to an 8 L polymerizer fitted with a stirrer.

Water 200 parts OSA 0.2 parts Disodium ethylenediaminetetraacetate 0.001 parts Ferrous sulfate 0.00025 parts Sodium formaldehydesulfoxylate 0.15 parts

After deoxidizing the inside of the polymerizer and heating the same to 60° C., the monomer mixture (a) shown in Table 1 and Table 2 was added dropwise successively at a rate of 10 parts/hour and polymerized for 30 minutes to obtain an acrylic ester rubber-like polymer. The degree of polymerization conversion was 99.5%. Then, after feeding 0.2 parts of OSA, and the monomer mixture (b) shown in Table 1 and Table 2 was added dropwise successively at a rate of 12 parts/hour and polymerized for 1 hour to obtain an acrylic graft copolymer (A) and a methacrylic polymer (B). The resultant latex was salted out and solidified with calcium acetate, rinsed and dried to obtain resin powder. The reduced viscosity and graft ratio of the resin powder were measured. The results are shown in Table 1 and Table 2.

Reference Example 19

A monomer mixture of 92% of MMA and 8% of BA was subjected to emulsion polymerization to prepare a copolymer. The reduced viscosity of the resultant methacrylic ester copolymer was 0.36 dl/g.

Reference Example 20

MMA-EA copolymer (Sumipex EX by Sumitomo Chemical: a copolymer consisting of about 95% of MMA and about 5% of EA, reduced viscosity 0.30 dl/g) prepared by suspension polymerization was used.

TABLE 1 Reference Example 1 2 3 4 5 6 7 8 9 OSA (parts) 0.20 0.24 0.18 0.28 0.35 0.20 0.15 0.05 0.20 Monomer (parts) 21 23 23 30 40 14 18 30 23 mixture BA (%) 90 90 90 90 90 98 90 90 90 (a) MMA (%) 7.6 8.0 7.5 6.5 8.0 — 7.0 7.5 8.6 AMA (%) 2.4 2.0 2.5 3.5 2.0 2.0 3.0 2.5 1.4 CHP (parts) 0.06 0.08 0.08 0.09 0.12 0.05 0.05 0.09 0.06 Monomer (parts) 79 77 77 70 60 86 82 70 77 mixture BA (%) 10 10 10 10 10 10 10 10 10 (b) MMA (%) 90 90 90 90 90 90 90 90 90 CHP (parts) 0.30 0.30 0.30 0.30 0.30 0.30 0.30 0.30 0.30 tDM (parts) 0.30 0.28 0.25 0.25 0.28 0.25 0.30 0.30 0.60 Reduced 0.35 0.32 0.36 0.39 0.36 0.38 0.34 0.28 0.15 viscosity Graft ratio 135 130 120 165 90 110 110 115 28

TABLE 2 Reference Example 10 11 12 13 14 15 16 17 18 OSA (parts) 0.20 0.15 0.24 0.28 0.26 0.26 0.20 0.20 0.26 Monomer (parts) 16 18 14 30 30 30 16 16 30 mixture BA (%) 90 90 98 90 89 89 90 90 89 (a) MMA (%) 7.6 7.4 — 7.5 8.0 7.5 9.0 8.6 8.0 AMA (%) 2.4 2.6 2.0 2.5 3 3.5 1.0 2.4 3.0 CHP (parts) 0.06 0.06 0.05 0.09 0.09 0.09 0.06 0.06 0.09 Monomer (parts) 84 82 86 70 70 70 84 84 70 mixture BA (%) 10 10 10 10 8 8 10 10 8 (b) MMA (%) 90 90 90 90 92 92 90 90 92 CHP (parts) 0.30 0.30 0.30 0.30 0.30 0.30 0.30 0.30 0.30 tDM (parts) 0.28 0.30 0.25 0.25 0.25 0.25 0.28 0.60 0.30 Reduced 0.35 0.32 0.38 0.32 0.39 0.39 0.34 0.15 0.33 viscosity Graft ratio 135 140 125 120 150 165 110 28 125

Examples 1 to 17 and Comparative Examples 1 to 7

Film was prepared in the following procedures using resin powders obtained in reference examples 1 to 20.

1.5 parts of TINUVIN 1577 (Ciba Specialty Chemicals Inc.) as a UV absorber and 0.3 parts of Sumilizer GM (Sumitomo Chemical) as an antioxidant were mixed into 100 parts of the resin composition of the formulation shown in Table 3 and Table 4 and extruded with a vented extruder at 220° C. to obtain extruded pellets. The resultant pellets were molded with a T-die extruder at die temperature of 240° C. to obtain film 100 μm thick. Various physical properties were evaluated using this film. The results are shown in Table 3 and Table 4.

TABLE 3 Examples 1 2 3 4 5 6 7 8 9 10 11 12 13 Resin Reference 100 compo- example 1 sition Reference 100 example 2 Reference 100 example 3 Reference 70 80 example 4 Reference 60 example 5 Reference 100 example 6 Reference 100 example 7 Reference example 8 Reference example 9 Reference 100 example 10 Reference 100 example 11 Reference 100 example 12 Reference 60 50 example 13 Reference example 14 Reference example 15 Reference example 16 Reference example 17 Reference example 18 Reference 20 50 example 19 Reference 30 40 40 example 20 Average particle 800 600 1200 780 780 800 800 800 800 1200 600 780 780 size (Å) of rubber-like polymer Amount of 2.4 2.0 2.5 3.5 3.5 2.0 2.0 3.0 2.4 2.6 2.0 2.5 2.5 crosslinking agent (parts) Content of 21 23 23 21 24 24 14 18 16 18 14 18 15 rubber-like polymer (%) Graft ratio (%) 135 130 120 165 165 90 110 110 135 140 125 120 120 Reduced viscosity 0.35 0.32 0.36 0.39 0.37 0.36 0.38 0.34 0.35 0.32 0.38 0.31 0.34 (dl/g) Tensile strength 55 57 54 60 50 51 76 63 65 61 71 62 68 (MPa) Elongation at the 100 90 120 100 120 100 50 70 70 80 60 65 60 time of tensile breakage (%) Stress-whitening ∘ ∘ ∘ ∘ ∘ ∘ ∘ ∘ ∘ Δ ∘ ∘ ∘ Transparency 0.6 0.4 0.9 0.6 0.6 0.8 0.3 0.5 0.3 0.6 0.3 0.4 0.3 (haze) (%) Transparency ∘ ∘ ∘ ∘ ∘ ∘ ∘ ∘ ∘ ∘ ∘ ∘ ∘ after heating Pencil hardness H H H H H H 2H H H H 2H H H Moldability of ∘ ∘ ∘ ∘ ∘ ∘ ∘ ∘ ∘ ∘ ∘ ∘ ∘ film Surface ∘ ∘ ∘ ∘ ∘ ∘ ∘ ∘ ∘ ∘ ∘ ∘ ∘ properties of film Processability of ∘ ∘ ∘ ∘ ∘ ∘ Δ Δ Δ ∘ Δ ∘ ∘ film

TABLE 4 Examples Comparative examples 14 15 16 17 1 2 3 4 5 6 7 Resin Reference compo- example 1 sition Reference example 2 Reference example 3 Reference example 4 Reference 100 example 5 Reference example 6 Reference example 7 Reference 70 60 10 example 8 Reference 100 example 9 Reference example 10 Reference example 11 Reference example 12 Reference 100 example 13 Reference 60 example 14 Reference 60 example 15 Reference 100 example 16 Reference 100 example 17 Reference 60 example 18 Reference 40 40 90 example 19 Reference 40 30 40 example 20 Average particle 800 800 780 780 2500 800 800 800 2500 2500 810 size (Å) of rubber-like polymer Amount of crosslinking 3.0 3.5 2.5 3.0 2.5 1.4 2.0 1.0 2.5 2.5 2.4 agent (parts) Content of rubber-like 18 18 30 18 21 23 40 16 18 3 16 polymer (%) Graft ratio (%) 150 165 90 125 115 28 90 110 115 115 28 Reduced viscosity 0.39 0.39 0.32 0.32 0.28 0.15 0.36 0.33 0.29 0.35 0.15 (dl/g) Tensile strength (MPa) 62 61 32 62 48 25 35 58 54 80 28 Elongation at 65 65 100 20 50 5 150 60 50 5 1 the time of tensile breakage (%) Stress-whitening ∘ ∘ ∘ ∘ x x ∘ x x x x Transparency 0.3 0.3 0.9 0.6 2.5 1.2 1.5 0.8 2.3 3.5 2.9 (haze) (%) Transparency ∘ ∘ ∘ ∘ x x Δ Δ x Δ x after heating Pencil hardness H H B H H H 3B H H 3H HB Moldability of film ∘ ∘ ∘ ∘ ∘ x ∘ ∘ ∘ x x Surface properties of ∘ ∘ Δ ∘ ∘ x ∘ Δ ∘ Δ x film Processability of film ∘ ∘ ∘ ∘ ∘ x ∘ ∘ Δ x x

Reference Examples 21 to 28

The following substances were fed to an 8 L polymerizer fitted with a stirrer.

Water 200 parts OSA 0.2 parts Disodium ethylenediaminetetraacetate 0.001 parts Ferrous sulfate 0.00025 parts Sodium formaldehydesulfoxylate 0.15 parts

After deoxidizing the inside of the polymerizer and heating the same to 60° C., the monomer mixture (a) shown in Table 5 was added dropwise successively at a rate of 10 parts/hour and polymerized for 30 minutes to obtain an acrylic ester rubber-like polymer. The degree of polymerization conversion was 99.5%. Then, after feeding 0.2 parts of OSA, and the monomer mixture (b) shown in Table 5 was added dropwise successively at a rate of 12 parts/hour in first and second steps and polymerized for 1 hour to obtain an acrylic graft copolymer (A) and a methacrylic polymer (B). The resultant latex was salted out and solidified with calcium acetate, rinsed and dried to obtain resin powder. The reduced viscosity and graft ratio of the resin powder were measured. The results are shown in Table 5.

TABLE 5 Reference examples 21 22 23 24 25 26 27 28 OSA (parts) 0.20 0.26 0.24 0.26 0.15 0.20 0.05 0.20 Monomer (parts) 18 30 16 30 30 16 30 16 mixture BA (%) 90 90 97 96.2 89 90 90 90 (a) MMA (%) 7.4 7.5 — — 8 9 7.5 8.6 AMA (%) 2.6 2.5 3.0 3.8 3.0 1.0 2.5 1.4 CHP (parts) 0.06 0.09 0.05 0.09 0.09 0.05 0.09 0.06 Monomer First step (parts) 42 40 50 35 30 54 35 44 mixture BA (%) 12 10 10 10 8 20 10 10 (b) MMA (%) 88 90 90 90 92 80 90 90 CHP (parts) 0.15 0.15 0.21 0.15 0.13 0.15 0.15 0.15 tDM (parts) 0.15 0.13 0.21 0.15 0.11 0.18 0.16 0.30 Second step (parts) 40 30 20 35 40 30 35 40 BA (%) 17 20 20 20 30 10 20 20 MMA (%) 83 80 80 80 70 90 80 80 CHP (parts) 0.15 0.15 0.09 0.15 0.17 0.15 0.15 0.30 tDM (parts) 0.15 0.12 0.09 0.15 0.14 0.10 0.16 0.15 Reduced viscosity 0.35 0.39 0.30 0.32 0.39 0.34 0.28 0.15 Graft ratio 135 145 140 120 150 110 115 28

Examples 18 to 24 and Comparative Examples 8 to 10

Film was prepared using each of the resin powders obtained in reference examples 19 to28 through the following procedure.

1.5 parts of TINUVIN 1577 (Ciba Specialty Chemicals Inc.) as a UV absorber and 0.3 parts of Sumilizer GM (Sumitomo Chemical) as an antioxidant were mixed into 100 parts of the resin composition of the formulation shown in Table 6 and extruded with a vented extruder at 220° C. to obtain extruded pellets. The resultant pellets were molded with a T-die extruder at die temperature of 240° C. to obtain film 100 μm thick. Various physical properties were evaluated using this film. The results are shown in Table 6.

TABLE 6 Examples Comparative examples 18 19 20 21 22 23 24 8 9 10 Resin Reference 50 90 compo- example 19 sition Reference 40 40 30 example 20 Reference 100 example 21 Reference 60 100 example 22 Reference 100 example 23 Reference 60 50 example 24 Reference 70 example 25 Reference 100 example 26 Reference 10 example 27 Reference 100 example 28 Average particle 800 780 600 780 1200 780 780 800 2500 800 size (Å) of rubber-like polymer Amount of crosslinking 2.6 2.5 3.0 3.8 3.0 3.8 2.5 1.0 2.5 1.4 agent (parts) Content of rubber-like 18 18 16 18 21 15 30 16 3 16 polymer (%) Graft ratio (%) 135 145 140 120 150 120 145 110 115 28 Reduced viscosity 0.35 0.35 0.30 0.31 0.37 0.34 0.39 0.34 0.35 0.15 (dl/g) Tensile strength (MPa) 61 63 65 62 55 67 32 70 85 68 Elongation at 70 68 90 100 110 95 110 50 15 10 the time of tensile breakage (%) Stress-whitening ∘ ∘ ∘ ∘ ∘ ∘ ∘ x x x Transparency (haze) (%) 0.6 0.5 0.4 0.6 0.8 0.5 0.9 0.8 3.5 2.6 Transparency ∘ ∘ ∘ ∘ ∘ ∘ ∘ Δ x x after heating Pencil hardness H H H H F 2H 2B H 3H HB Moldability of film ∘ ∘ ∘ ∘ ∘ ∘ ∘ ∘ Δ x Surface properties of ∘ ∘ ∘ ∘ ∘ ∘ Δ Δ x x film Processability ∘ ∘ ∘ ∘ ∘ ∘ ∘ ∘ x x of film

INDUSTRIAL APPLICABILITY

According to the present invention, a film can be obtained which undergoes less stress-whitening even by molding at low temperatures, which has high surface hardness, excellent transparency, also excellent transparency even after heating and excellent weatherability, whose elongation at the time of tensile breakage is high, and whose moldability, surface properties and processability (cracks are less likely to occur at the time of film cutting) are all excellent. 

1. An acrylic film, composed of a resin composition (C) that comprises an acrylic graft copolymer (A) containing an acrylic ester rubber polymer and a methacrylic polymer (B) containing 80% by weight or more of methyl methacrylate, wherein (1) the content of the acrylic ester rubber polymer in the resin composition (C) is 5% by weight or more and 30% by weight or less, (2) the average particle size of the acrylic ester rubber polymer is 500 to 2000 Å, (3) the relationship between the average particle size d (Å) of the acrylic ester rubber polymer and the amount w (% by weight) of a cross-linking agent used in the acrylic ester rubber polymer satisfies the following equation: 0.0025d≦w≦0.0045d, (4) the graft ratio of the acrylic graft copolymer (A) is 30% or more and 200% or less, and (5) the reduced viscosity of methyl ethyl ketone soluble matter in the resin composition (C) is 0.2 to 0.8 dl/g.
 2. The acrylic film according to claim 1, wherein the content of the acrylic ester rubber polymer in the resin composition (C) is 15% by weight or more and 30% by weight or less.
 3. The acrylic film according to claim 1, wherein the content of the acrylic ester rubber polymer in the resin composition (C) is more than 20% by weight and 30% by weight or less.
 4. The acrylic film according to claim 1, wherein the acrylic graft copolymer (A) is prepared by: graft polymerizing a monomer mixture containing 86% by weight or more of a methacrylic ester onto the acrylic ester rubber polymer in a first step; and graft polymerizing a monomer mixture containing 85% by weight or less of a methacrylic ester onto the resultant graft polymer in a second step.
 5. A laminate containing the acrylic film according to claim
 1. 6. The laminate according to claim 5, produced by injection molding. 